What Is Stainless Steel 310S Pipe Fittings?
These Stainless steel 310S pipe fittings help in the conveyance of fluids and gases in different conditions. The 310 SS buttweld fittings possess enhanced strength and are suitable to work in stress-induced conditions. Our buttweld fittings offer a seamless flow in the system and can be availed at reasonable prices at all our outlets.
ASTM A403 WP310S Pipe Bend Manufacturer in India in Sizes Range 1/2" To 24"
ASTM A403 WP310S end cap helps in closing the ends of the system. These caps protect the piping grades as they are stored or transported against damage or corrosive affluents. A 310S SS stub end is a short piece that allows it to minimize the weight of high-grade material to save costs. These ends secure the joints of pressurized pipes utilizing a good fastener set.
Table of Content
- ASTM A403 WP310S Pipe Bend Application
- SS 310S Fittings Creep Properties
- Stainless Steel 310S Pipe Fittings Specification
- Popular Types of Stainless Steel 310S Buttweld Fittings
- SS 310S Pipe Fittings Heat Treatment
- A403 WP310S Fittings Equivalent Grade
- 310S SS Pipe Fittings Chemical Composition
- UNS S31008 Seamless Fittings Mechanical Properties
- WNR EN 1.4845 Weld Fittings Physical Properties
Testing: Hyrdrostatic Test
Bending Method: Hot Induction Bending
Find the Best-Quality UNS S31008 Elbow and Reducer Supplier in Mumbai Used for Low Pressure Applications
View SS 310S Fittings Creep properties and Specification as per ASME B16.9
| Temperature in °C | Creep Strain (MPa) in 1000 H |
|---|---|
| 600°C | 120 |
| 700°C | 50 |
| 800°C | 20 |
| 900°C | 10 |
| 1000°C | 5 |
Most Selling Size :
- DN15 To DN1500
- Welded : 24" To 96"
- Seamless : 1/2" To 24"
- Buttweld : 1/2" To 36"
- Contact stainless steel 310S pipe fittings manufacturer in India for above 48″
Available Machines :
- CNC
- Beveling Machine
- Conventional Machine
Documentation List :
- Fumigation certificates
- Raw material test reports
- Material traceability records
Common Thickness :
- SCH 20 & 40
- SCH : 80 To 120
- SCH : 160 To 180
Manufacturing Standard :
- ASME B16.9
- ASME B16.28
- DIN/ JIS/ EN/ ISO
Types Of Packaging :
- Carton Box
- Wooden Cases
- Wooden Pallet
Melting Point :
- 1400°C To 1455°C
Hardness :
- Brinell (HB) = 217 Max.
Density :
- 7.84 (Mg/m3)
Applicable Fluids :
- Water and Air
- Steam
- Oil and Gas
Forming Technique :
- Hot formed
- Cold formed
Surface Finish :
- Polished
ISO Standard :
- ISO 5251
Most Demanded Types :
- End Cap/ Stub End
- Pipe Bend/ Pipe Cross
- Elbow/ Tee/ Reducer
Method :
- Welded (Weld)
- Seamless (SMLS)
- Buttweld (BW)
Sour Service :
- NACE TM-0284
- NACE MR0103
- NACE MR0175
Thickness Tolerance :
- Custom
- +/-12.5%
Marking Formula :
- Size & Schedule
- Grade & Material
- Manufacturers Name
- Standard & Heat No.
Life :
- Stainless Steel = 45 To 50 Years
Manufacturing Process :
- Forged
- Machined
- Heat Treated
Connection :
- Welding
Process :
- Cutting
- Bending
- Welding
Test Certificates :
- EN 10204 3.1
- EN 10204 3.2
Types Of Ends :
- Compound Bevel
- Bevelled
- Plain Bevel
Use For :
- Chemical Equipment
- Petrochemicals
- Oil and Gas
- Power Generation
- Pharmaceuticals
Technique :
- Butt Weld
- Welding
- Forged
- Casting
- Pushing
Inspection Plan :
- PMI Test
- Mechanical Testing
- Chemical Analysis
- Hyrdrostatic Test
- Hardness Test
Bend Radius :
- 1.5D/ 2D/ 3D
- 4D/ 5D/ 6D
- 8D/ 10D/ 22D
Pipe Bend Angle:
- 15 Deg, 22.5 Deg, 30 Deg
- 45 Deg, 60 Deg, 90 Deg
- 135 Deg, 180 Deg
Method Of Bending :
- Roll bending
- Rotary draw bending
- Hot induction bending
Logistics :
- By Sea
- By Air
- France = 30 day
- Indonesia = 9 days
- UAE = 5 day
- Italy = 30 day
- Malaysia = 10 days
- Philippines = 14 day
Maximum Size :
- DN2000
- 120 Inch
Value Added Services :
- Polishing
- Cutting
- Minor Fabrication
- Threading
- Beveling End
Stainless Steel 310S Elbow
ASTM A403 WP310S Reducer
SS 310S Stub End
UNS S31008 Tee
DIN 1.4845 End Cap
A403 Grade WP310S Pipe Bend
Since 27 Years, Experts in Manufacturing 310S Stainless Steel Tee and Stub End for High Temperature, Check Heat Treatment
-
Solution treatment (Annealing)
-
2012°F To 2102°F
UNS :
- UNS S31008
Werkstoff No :
- 1.4845
JIS (Japan) :
- SUS 310S
BS (England) :
- 310S16
AFNOR (France) :
- -
EN (European) :
- X8CrNi25-21
GOST (Russian) :
- 20Ch23N18
Produce and Stock WNR 1.4845 End Cap in a Variety of Schedule like 10S, 20S, 40S and 80. Check Chemical Composition
![Carbon [C] :](imginfo/carbon.jpg "Carbon [C] :")
Carbon [C] :
- 0.08%
![Manganese [Mn] :](imginfo/manganese.jpg "Manganese [Mn] :")
Manganese [Mn] :
- 2.00%
![Phosphorus [P] :](imginfo/phosphorus.jpg "Phosphorus [P] :")
Phosphorus [P] :
- 0.045%
![Silicon [Si] :](imginfo/silicon.jpg "Silicon [Si] :")
Silicon [Si] :
- 1.50%
![Chromium [Cr] :](imginfo/chromium.jpg "Chromium [Cr] :")
Chromium [Cr] :
- 24.0 To 26.0%
![Nitrogen [N] :](imginfo/nitrogen.jpg "Nitrogen [N] :")
Nitrogen [N] :
- -
![Nickel [Ni] :](imginfo/nickel.jpg "Nickel [Ni] :")
Nickel [Ni] :
- 19.0 To 22.0%
Iron :
- Balance
Sulphur (S) :
- 0.030%
Tensile Strength :
- 515 MPa (Min.)
Yield Strength 0.2% Proof :
- 205 MPa Min.
Brinell (HB) :
- 217 Mix.
Elongation :
- 40%
Density :
- 7750 kg/m3
Elastic Modulus :
- 200 GPa
Specific Heat 0-100°C :
- 500 J/kg.K
Electrical Resistivity :
- 720 nΩ.m